Mechnical Composition

 

Mechnical Composition

MECHANICAL PROPERTIES

Grade

Tensile
Strength Mpa, (Min)

Yield
Strength 
Mpa, (Min)

%Age
Elongation
in 50mm
gauge length min

Hardness (Max)

BHN

Rb

301

515

205

40

217

95

304

515

205

40

201

92

304L

485

170

40

201

92

310S

515

205

40

217

95

316

515

205

40

217

95

316L

485

170

40

217

95

317

515

205

35

217

95

317L

515

205

40

217

95

321

515

205

40

217

95

347

515

205

40

201

92

409

380

170

20

179

88

409M

430

275

20

187

90

410S

415

205

22

183

89

410

450

205

20

217

89

420

700( max )

-

15

217

95

430

450

205

22

183

89

JSL AUS

515

205

40

217

95

JS- 203

515

205

40

217

95

301M

515

205

40

217

95

Hastelloy C - 22

Product Form Tensile (ksi) .2% Yield (ksi) Elongation % Hardness (HRb)
Plate (.25”-1.75”) 112 53 62 89
Sheet (.038”-.15”) 122 63 54 93
Bar (.50”-5.50”) 115 55 60 89

Hastelloy C - 276

Product Form Tensile (ksi) .2% Yield (ksi) Elongation %
Bar 110.0 52.6 62
Plate 107.4 50.3 67
Sheet 115.5 54.6 60
Tube & Pipe 105.4 45.4 70

Inconel 600

Product Form Condition Tensile (ksi) .2% Yield (ksi) Elongation (%) Hardness (HRB)
Rod & Bar Cold-Drawn 80-100 25-50 35-55 65-85
Rod & Bar Hot-Finished 80-100 30-50 35-55 65-85
Tube & Pipe Hot-Finished 75-100 25-50 35*55 -
Tube & Pipe Cold-Drawn 80-100 25-50 35-55 88 Max
Plate Hot-Rolled 80-105 30-50 35-55 65-85
Sheet Cold-Drawn 80-100 30-45 35-55 88 Max

Inconel 625

Temp° F Tensile (psi) .2% Yield (psi) Elongation in 2 “ (%)
70 144,000 84,000 44
400 134,000 66,000 45
600 132,000 63,000 42.5
800 131,500 61,000 45
1000 130,000 60,500 48
1200 119,000 60,000 34
1400 78,000 58,500 59
1600 40,000 39,000 117

Incoloy 800H / HT

Product Tensile (ksi) .2% Yield (ksi) Elongation (%)
Rod & Bar 75-100 30-60 60-30

Incoloy 825

Tensile (ksi) .2% Yield (ksi)
85 30-35

Monel 400

Product Form Condition Tensile (ksi) .2% Yield (ksi) Elongation (%) Hardness (HRB)
Rod & Bar Annealed 75-90 25-50 60-35 60-80
Rod & Bar Cold-Drawn Stress Relieved 84-120 55-100 40-22 85-20 HRC
Plate Annealed 70-85 28-50 50-35 60-76
Sheet Annealed 70-85 30-45 45-35 65-80
Tube & Pipe Seamless Annealed 70-85 25-45 50-35 75 max *


Monel K - 500

Product Form
Condition
Tensile (ksi)
.2% Yield (ksi)
Elongation %
Hardness
Rod & Bar
Hot-Finished/Aged
140-190
100-150
30-20
27-38 HRC
Rod & Bar
Hot Finished/Annealed
90-110
40-60
45-25
75-90 HRB
Rod & Bar
Hot Finished/Annealed/Aged
130-165
85-120
35-20
24-35 HRC
Rod & Bar
Cold-Drawn/Aged
135-185
95-160
30-15
25-41 HRC
Rod & Bar
Cold-Drawn/Annealed/Aged
130-190
85-120
30-20
24-35 HRC
Plate
Hot-Finished/Aged
140-180
100-135
30-20
27-37 HRC
Sheet
Cold-Rolled/Annealed
90-105
40-65
45-25
85 HRB Max

Nickel 200 /201

Material Form and Condition Tensile (ksi) .2% Yield (ksi) Elongation (%) Hardness (HRB)
Rod & Bar Hot Finished 60-85 15-45 55-35 45-80
Rod & Bar Cold Drawn/Annealed or Hot-Finished/Annealed 55-75 15-30 55-40 45-70
Plate Hot-Rolled/Annealed 55-80 15-40 60-40 45-75
Sheet Annealed 55-75 15-30 55-40 70 max
Tube & Pipe Seamless Annealed 55-75 12-30 60-40 70 max

Titanium

Titanium Grade 2

Hardness, Knoop 170 170  
Hardness, Rockwell B 80 80  
Hardness, Vickers 145 145  
Tensile Strength, Ultimate 344 MPa 49900 psi  
Tensile Strength, Yield 275 - 410 MPa 39900 - 59500 psi  
Elongation at Break 20 % 20 %  
Reduction of Area 35 % 35 %  
Modulus of Elasticity 105 GPa 15200 ksi In Tension
Compressive Modulus 110 GPa 16000 ksi  
Poisson's Ratio 0.37 0.37  
Izod Impact 114 - 171 J 84.1 - 126 ft-lb  
Fatigue Strength 300 MPa 43500 psi 1E+7 cycles, Unnotched
Fatigue Strength 425 MPa 61600 psi 30,000 cycles, Unnotched
Fracture Toughness 66 MPa-m½ 60.1 ksi-in½ K(Q); annealed
Shear Modulus 45 GPa 6530 ksi  

Titanium Grade 5

Hardness, Brinell 379 379
Hardness, Knoop 414 414
Hardness, Rockwell C 41 41
Hardness, Vickers 396 396
Tensile Strength, Ultimate 1170 MPa 170000 psi
Tensile Strength, Yield 1100 MPa 160000 psi
Elongation at Break 10 % 10 %
Modulus of Elasticity 114 GPa 16500 ksi
Compressive Yield Strength 1070 MPa 155000 psi
Notched Tensile Strength 1550 MPa 225000 psi
Ultimate Bearing Strength 2140 MPa 310000 psi
Bearing Yield Strength 1790 MPa 260000 psi
Poisson's Ratio 0.33 0.33
Charpy Impact 23 J 17 ft-lb
Fatigue Strength 160 MPa 23200 psi
Fatigue Strength 700 MPa 102000 psi
Fracture Toughness 43 MPa-m½ 39.1 ksi-in½
Shear Modulus 44 GPa 6380 ksi
Shear Strength 760 MPa 110000 psi

Titanium Grade 7

Hardness, Brinell 200 200
Hardness, Knoop 222 222
Hardness, Rockwell B 75 75
Hardness, Rockwell C 11 11
Hardness, Vickers 209 209
Tensile Strength, Ultimate 344 MPa 49900 psi
Tensile Strength, Yield 275 - 410 MPa 39900 - 59500 psi
Elongation at Break 20 % 20 %
Modulus of Elasticity 105 GPa 15200 ksi
Compressive Modulus 110 GPa 16000 ksi
Poisson's Ratio 0.37 0.37
Shear Modulus 45 GPa 6530 ksi